Micro-Shear Bond Strength of Indirect Composite Resin to Three Different Computer-Milled Cores After Thermocycling
Somayeh Zeighami1, Safoura Ghodsi1, Naghmeh Musapoor *2
1- Associate Professor, Dental Research Center, Dentistry Research Institute and Department of Prosthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
2- Postgraduate Student, Department of Prosthodontics, School of Dentistry, Gilan University of Medical Sciences, Rasht, Iran
Abstract:   (256 Views)
Background and Aim: The aim of this study was to evaluate the micro-shear bond strength of an indirect composite resin to three different types of cores.
Materials and Methods: In this in-vitro study, 14 blocks (5×5×2 mm) were designed and milled by computer from cobalt-chromium (Co-Cr) alloy, zirconia, and polyether ether ketone (PEEK). Each sample was treated according to the manufacturer’s instructions, and the appropriate primer, and a layer of Crea.lign opaquer were applied on the surface. For micro-shear bond strength test, a plastic tube with an internal diameter of 1 mm and height of 2 mm was placed on each block, and Crea.lign paste was condensed in it. The Crea.lign paste and opaquer were light-cured separately for 180 s, and finally for 360 s. All samples were placed in 37°C distilled water for 24 h and thermocycled for 5000 cycles (5 to 55°C). The microtensile tester machine was used to measure the micro-shear bond strength. The samples were also evaluated for failure modes. Data were analyzed using one-way ANOVA (P<0.05).
Results: According to one-way ANOVA, the mean micro-shear bond strength (MPa) in Co-Cr alloy, zirconia, and PEEK groups was 25.19±5.53, 23.49±5.48, and 20.58±5.68 MPa, respectively. There was no significant difference in micro-shear bond strength of the three groups (P= 0.099). The most frequent mode of failure in all three groups was adhesive, followed by mixed, and cohesive.
Conclusion: Applying the standard procedure, type of core material had no significant effect on the micro-shear bond strength of Crea.lign composite veneer.
Keywords: Chromium Alloys, Composite Resins, Polyetheretherketone, Shear Strength, Zirconium Oxide
Full-Text [PDF 737 kb]   (69 Downloads)    
Type of Study: Orginal | Subject: Porosthodontics
Add your comments about this article
Your username or Email:

CAPTCHA


XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Zeighami S, Ghodsi S, Musapoor N. Micro-Shear Bond Strength of Indirect Composite Resin to Three Different Computer-Milled Cores After Thermocycling. J Islam Dent Assoc Iran. 2020; 32 (3 and 4) :67-74
URL: http://jidai.ir/article-1-2117-en.html


Volume 32, Issue 3 And 4 (10-2020) Back to browse issues page
Journal of Islamic Dental Association of Iran

AWT IMAGE

This work is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported License which allows users to read, copy, distribute and make derivative works for non-commercial purposes from the material, as long as the author of the original work is cited properly

Persian site map - English site map - Created in 0.05 seconds with 29 queries by YEKTAWEB 4280